Shimano Kairiki 8 : 8lb BRAID
Kairiki 8 from Shimano adopts the new VT construction braiding technology. Featuring 8 carriers and incorporating premium Japanese manufacturing, the new tight weave VT construction is created through applying high tension at opposing directions during the braiding process. During the VT Construction Method, the braid fibre is woven evenly at all angles – resulting in a smoother finish and reduced diameter. The casting performance of the line is significantly improved as the smooth finish creates less friction through the guides and cast noise is also reduced. The tight weave achieves enhanced sensitivity achieved through the lower stretch. These attributes make Kairiki 8 an excellent choice when high sensitivity and castability are all required to give that extra edge against your target species.
https://www.shimanofish.com.au/content/fish/oceania/au/en/homepage/productdetail.P-KAIRIKI_8.html
Key Statistics
- Measured Diameter: .194mm (194% on stated .100mm)
- Measured Breaking Strain: 15.55lbs (194% of rated 8lbs)
- Abrasion Breaking Strain: 2.73lbs (17.56% of max break)
- FG Knot Breaking Strain: 8.15lbs (52.41% of max break)
Testing Process
Key Line Statistics
| Attribute | Value |
|---|---|
| Brand | Shimano |
| Name | Kairiki 8 |
| Web Site | Visit Website |
| Rated Strength (lbs) | 8 |
| Date Tested | 15 April 2023 |
| Credit to | @moistieoystie |
| Strands | 8 |
| Cost $AUD | 36.99 |
| Spool Quanity (m) | 150 |
| Quoted Diameter (mm) | 0.1 |
| Measured Average Diameter (mm) | 0.195 |
| Diameter Quoted vs Measured (%) | 195 |
| Minimum Diameter (mm) | 0.184 |
| Maximum Diameter (mm) | 0.21 |
| Break Max Average (lbs) | 15.55 |
| Claimed vs Actual Breaking Strain (%) | 194.42 |
| Average Stretch @ Maximum Break | N/A |
| Tensile Strength (PSI) | 337074 |
| Tensile Rank | 59 |
| Abrasion Break Max Average (lbs) | 2.73 |
| Abrasion Break vs Max Break Strain (%) | 17.53 |
| Abrasion % of Maximum Rank | 124 |
| Abrasion Tensile Strength PSI | 59178 |
| Abrasion Tensile Rank | 122 |
| FG Break Max Average (lbs) | 8.15 |
| FG Break vs Max Break Strain (%) | 52.41 |
| FG % of Maximum Rank | 88 |
| FG Tensile Strength PSI | 176666 |
| FG Tensile Rank | 85 |
| Time | Test1 | Test2 | Test3 | Average | Rated |
|---|---|---|---|---|---|
| 0.0 | 0.00 | 0.00 | 0.00 | 15.55 | 8 |
| 0.1 | 0.49 | 0.29 | 0.09 | 15.55 | 8 |
| 0.2 | 0.93 | 0.73 | 0.30 | 15.55 | 8 |
| 0.3 | 1.12 | 1.01 | 0.46 | 15.55 | 8 |
| 0.4 | 1.31 | 1.50 | 0.97 | 15.55 | 8 |
| 0.5 | 1.63 | 1.71 | 1.30 | 15.55 | 8 |
| 0.6 | 1.94 | 1.91 | 1.99 | 15.55 | 8 |
| 0.7 | 2.57 | 2.20 | 2.33 | 15.55 | 8 |
| 0.8 | 2.87 | 2.50 | 2.68 | 15.55 | 8 |
| 0.9 | 3.37 | 3.05 | 2.89 | 15.55 | 8 |
| 1.0 | 3.57 | 3.32 | 3.11 | 15.55 | 8 |
| 1.1 | 3.76 | 3.74 | 3.60 | 15.55 | 8 |
| 1.2 | 4.01 | 3.89 | 3.87 | 15.55 | 8 |
| 1.3 | 4.27 | 4.29 | 4.40 | 15.55 | 8 |
| 1.4 | 4.75 | 4.53 | 4.65 | 15.55 | 8 |
| 1.5 | 4.99 | 4.77 | 4.90 | 15.55 | 8 |
| 1.6 | 5.36 | 4.98 | 5.12 | 15.55 | 8 |
| 1.7 | 5.51 | 5.18 | 5.34 | 15.55 | 8 |
| 1.8 | 5.85 | 5.53 | 5.71 | 15.55 | 8 |
| 1.9 | 6.05 | 5.67 | 5.85 | 15.55 | 8 |
| 2.0 | 6.25 | 6.02 | 6.19 | 15.55 | 8 |
| 2.1 | 6.41 | 6.23 | 6.39 | 15.55 | 8 |
| 2.2 | 6.58 | 6.63 | 6.58 | 15.55 | 8 |
| 2.3 | 6.85 | 6.81 | 6.76 | 15.55 | 8 |
| 2.4 | 6.97 | 7.00 | 6.95 | 15.55 | 8 |
| 2.5 | 7.23 | 7.11 | 7.24 | 15.55 | 8 |
| 2.6 | 7.38 | 7.23 | 7.34 | 15.55 | 8 |
| 2.7 | 7.53 | 7.51 | 7.63 | 15.55 | 8 |
| 2.8 | 7.67 | 7.69 | 7.80 | 15.55 | 8 |
| 2.9 | 7.82 | 8.02 | 8.15 | 15.55 | 8 |
| 3.0 | 8.05 | 8.18 | 8.33 | 15.55 | 8 |
| 3.1 | 8.14 | 8.34 | 8.50 | 15.55 | 8 |
| 3.2 | 8.38 | 8.47 | 8.61 | 15.55 | 8 |
| 3.3 | 8.53 | 8.59 | 8.73 | 15.55 | 8 |
| 3.4 | 8.82 | 8.90 | 9.01 | 15.55 | 8 |
| 3.5 | 8.96 | 9.09 | 9.17 | 15.55 | 8 |
| 3.6 | 9.10 | 9.43 | 9.48 | 15.55 | 8 |
| 3.7 | 9.20 | 9.59 | 9.62 | 15.55 | 8 |
| 3.8 | 9.31 | 9.85 | 9.76 | 15.55 | 8 |
| 3.9 | 9.46 | 9.95 | 9.85 | 15.55 | 8 |
| 4.0 | 9.50 | 10.05 | 9.94 | 15.55 | 8 |
| 4.1 | 9.61 | 10.21 | 10.17 | 15.55 | 8 |
| 4.2 | 9.67 | 10.36 | 10.30 | 15.55 | 8 |
| 4.3 | 9.82 | 10.66 | 10.57 | 15.55 | 8 |
| 4.4 | 9.90 | 10.80 | 10.69 | 15.55 | 8 |
| 4.5 | 9.99 | 11.06 | 10.90 | 15.55 | 8 |
| 4.6 | 10.08 | 11.17 | 10.99 | 15.55 | 8 |
| 4.7 | 10.16 | 11.45 | 11.07 | 15.55 | 8 |
| 4.8 | 10.41 | 11.62 | 11.19 | 15.55 | 8 |
| 4.9 | 10.56 | 11.78 | 11.30 | 15.55 | 8 |
| 5.0 | 10.82 | 11.92 | 11.57 | 15.55 | 8 |
| 5.1 | 10.93 | 12.05 | 11.71 | 15.55 | 8 |
| 5.2 | 11.03 | 12.26 | 11.94 | 15.55 | 8 |
| 5.3 | 11.16 | 12.34 | 12.01 | 15.55 | 8 |
| 5.4 | 11.28 | 12.51 | 12.09 | 15.55 | 8 |
| 5.5 | 11.49 | 12.62 | 12.22 | 15.55 | 8 |
| 5.6 | 11.57 | 12.79 | 12.34 | 15.55 | 8 |
| 5.7 | 11.75 | 12.85 | 12.57 | 15.55 | 8 |
| 5.8 | 11.85 | 12.92 | 12.66 | 15.55 | 8 |
| 5.9 | 11.95 | 12.97 | 12.85 | 15.55 | 8 |
| 6.0 | 12.08 | 13.03 | 12.94 | 15.55 | 8 |
| 6.1 | 12.21 | 13.09 | 13.16 | 15.55 | 8 |
| 6.2 | 12.50 | 13.10 | 13.30 | 15.55 | 8 |
| 6.3 | 12.67 | 13.18 | 13.43 | 15.55 | 8 |
| 6.4 | 12.92 | 13.24 | 13.54 | 15.55 | 8 |
| 6.5 | 13.00 | 13.31 | 13.65 | 15.55 | 8 |
| 6.6 | 13.22 | 13.37 | 13.84 | 15.55 | 8 |
| 6.7 | 13.35 | 13.42 | 13.92 | 15.55 | 8 |
| 6.8 | 13.48 | 13.58 | 14.11 | 15.55 | 8 |
| 6.9 | 13.57 | 13.69 | 14.23 | 15.55 | 8 |
| 7.0 | 13.65 | 13.88 | 14.34 | 15.55 | 8 |
| 7.1 | 13.84 | 13.98 | 14.46 | 15.55 | 8 |
| 7.2 | 13.94 | 14.19 | 14.59 | 15.55 | 8 |
| 7.3 | 14.18 | 14.31 | 14.81 | 15.55 | 8 |
| 7.4 | 14.31 | 14.43 | 14.90 | 15.55 | 8 |
| 7.5 | 14.61 | 14.54 | 15.15 | 15.55 | 8 |
| 7.6 | 14.77 | 14.66 | 15.29 | 15.55 | 8 |
| 7.7 | 14.93 | 14.81 | 15.56 | 15.55 | 8 |
| 7.8 | 15.01 | 14.86 | 15.67 | 15.55 | 8 |
| 7.9 | 15.08 | 14.90 | 15.79 | 15.55 | 8 |
| 8.0 | 15.16 | 15.83 | 15.55 | 8 | |
| 8.1 | 15.87 | 15.55 | 8 | ||
| 8.2 | 15.99 | 15.55 | 8 | ||
| 8.3 | 16.07 | 15.55 | 8 | ||
| 8.4 | 16.24 | 15.55 | 8 | ||
| 8.5 | 16.33 | 15.55 | 8 | ||
| 8.6 | 16.42 | 15.55 | 8 | ||
| 8.7 | 16.48 | 15.55 | 8 | ||
| 8.8 | 16.54 | 15.55 | 8 | ||
| 8.9 | 16.60 | 15.55 | 8 | ||
| 9.0 | 16.60 | 15.55 | 8 | ||
| 9.1 | 16.60 | 15.55 | 8 |